RESUMO
This in vitro study evaluated the effects of three polishing systems on the surface roughness of two ceromers. Material and Methods: 96 specimens (8 mmin diameter and 2 mm thick) were prepared in a metal mold using two restorative materials: CERAMAGE Shofu, Japan) and VMLC VITA (VITA Zahnfabrik,Germany). The specimens were divided into 4 groups(n=12): G1: positive control, Mylar strip; G2: abrasive tips, Edenta system; G3: silicon tips, Enhance system; and G4: abrasive tips, Shofu system. The parameter evaluated was the average surface roughness (Ra) determined by using a profilometer SJ 301 (Mitutoyo,Japan), followed by photographic evaluation image sthrough Scanning Electron Microscopy (SEM), witha 1000x magnification range. The data was subjected to statistical analysis for comparison between the groups (ANOVA, Tukey and Student T-tests), with a significance level of 5%. Results: there was a statistically significant difference between the siliconetip Enhance and the other groups for both ceromers with higher values of surface roughness. There was no statistically significant difference between the ceromers, except for the Shofu system, which showed lower values of surface roughness for Vita VMLC. Conclusion: With in the limitations of this study, itwas concluded that the Edenta and Shofu abrasive tipsare more effective in reducing the surface roughnessof ceromers compared with the Enhance silicone tip...
Avaliar o efeito de três sistemas de polimento na rugosidade superficial de 2 cerômeros. Material e Métodos: Foram confeccionados 96 corpos de prova divididos em 8 grupos: G1 e G5, controle positivo (matriz de poliéster), G2 e G6 (pontas abrasivas Edenta); G3 e G7 (pontas siliconadas Enhance); G4 e G8 (sistema Shofu).O parâmetro avaliado foi a média aritmética da rugosidade superficial (Ra) determinada em rugosimetro SJ 301 (Mitutoyo, Japão), seguida de avaliação fotográfica através da microscopia eletrônica de varredura (MEV), com o aumento de 1000 vezes. Os dados obtidos foram submetidos à análise estatística para comparação entre os grupos(ANOVA, Tukey e t-student pareado), nível de significância de 5%. Resultados: Houve diferença estatística significativa entre a ponta siliconada Enhance e os demais grupos, em ambos cerômeros, apresentando maiores valores de rugosidade superficial. Entre os polimentos avaliados, o único que diferiu entre os cerômeros foi o sistema Shofu que apresentou menores valores de rugosidade superficial para a Vita VMLC. Conclusão: Dentro das limitações do presente estudo, concluiu-seque as pontas abrasivas EDENTA e Shofu são mais eficazes na redução da rugosidade da superficial de cerômeros comparação com a ponta de silicone Enhance...
Assuntos
Humanos , Polimento Dentário , ResinasRESUMO
Objective: The purpose of this study was to evaluate the effect of finishing and polishing on color stability of a nanofilled composite resin (Filtek Z350 XT) according to different immersion media. Material and Method: Composite disks (10 mm diameter, 2 mm thickness) were prepared for each group (n = 6) using a stainless steel mold. The groups were divided according to the presence or absence of finishing and polishing procedure and immersion media (artificial saliva, artificial juice- KAPO(r) Coca-Cola(r) flavors: pineapple, orange, strawberry and grape). The finishing and polishing procedures were performed using Super -Snap(r) disks. The specimens were stored in artificial saliva for 24 hours (baseline) and were analyzed using a color spectrophotometer by CIELab system. Then, they were immersed in different media for 5 minutes, 3 times a day, every 4 hours during 60 days. They were stored in artificial saliva at 37 ± 1°C during the immersion intervals. After this time, new measure of color was performed. The data were analyzed using Kruskall-Wallis test and Mann- Whitney test. The significance level was 5%. Result: The results showed that the finishing/polishing not significantly influence the color stability of resin composite (p >0.05). There was no statistically significant difference in the color stability of the studied resin after immersion in different media (p > 0.05). Conclusion: The finishing and polishing procedures and the immersion media did not have influence on color stability of nanofilled resin Filtek Z350 XT. .
Objetivo: O objetivo deste estudo foi avaliar o efeito do acabamento e polimento na estabilidade de cor da resina nanoparticulada Filtek Z350 XT em função de diferentes meios de imersão. Material e Método: Espécimes circulares (10 mm de diâmetro e 2 mm de espessura) foram preparados para cada grupo (n=6) utilizando uma matriz de aço inoxidável. Os grupos experimentais foram divididos de acordo com a presença ou ausência de acabamento e polimento e diferentes meios de imersão (saliva artificial, Suco artificial pronto KAPO(r) da Coca Cola(r) sabores: abacaxi, laranja, morango e uva). Os procedimentos de acabamento e polimento foram realizados com discos de lixa Super-Snap(r). Os espécimes permaneceram em saliva artificial por 24 horas (baseline) e foram submetidos à análise da cor usando um espectrofotômetro pelo sistema CIELab. Em seguida, foram imersos nos diferentes meios por 5 minutos, 3 vezes ao dia, com intervalos de 4 horas, durante 60 dias. Os espécimes foram mantidos em saliva artificial a 37±1°C nos intervalos entre as imersões. Após este período foi realizada nova leitura de cor. Os dados foram analisados com os testes de Kruskall-Wallis e Mann-Whitney. O nível de significância foi de 5%. Resultado: Os resultados mostraram que o acabamento/polimento não influenciou significativamente a estabilidade de cor da resina composta (p>0,05). Não houve diferença estatisticamente significativa na estabilidade de cor da resina estudada após a imersão nos diferentes meios (p>0,05). Conclusão: O acabamento e polimento e os meios de imersão não apresentaram influência na estabilidade de cor da resina nanoparticulada Filtek Z350 XT. .